| S/N . | Effects . | Optimum combination . | Predicted Opt. effect . | Confirmed Opt. effect . | Diff. . | Con. Int. . | % Error . | |||
|---|---|---|---|---|---|---|---|---|---|---|
| A . | B . | C . | D . | |||||||
| 1. | Tensile Strength | 20% | 15% | 25 mm | 10% | 82.36 MPa | 80.1 MPa | 2.26 MPa | ±5.134 MPa | 2.74 |
| 2. | Flexural Strength | 40% | 15% | 35 mm | 5% | 68.6 MPa | 68.3 MPa | 0.3 MPa | ±0.95 MPa | 0.44 |
| 3. | Impact Strength | 40% | 15% | 25 mm | 35% | 46.1 kJ/m2 | 39.7 kJ/m2 | 6.4 kJ/m2 | ±9.35 kJ/m2 | 13.88 |
| 4. | Density | 10% | 5% | 5 mm | 15% | 0.5765g/cm3 | 0.5701g/cm3 | 0.0064g/cm3 | 0.0473g/cm3 | 1.11 |
| S/N . | Effects . | Optimum combination . | Predicted Opt. effect . | Confirmed Opt. effect . | Diff. . | Con. Int. . | % Error . | |||
|---|---|---|---|---|---|---|---|---|---|---|
| A . | B . | C . | D . | |||||||
| 1. | Tensile Strength | 20% | 15% | 25 mm | 10% | 82.36 MPa | 80.1 MPa | 2.26 MPa | ±5.134 MPa | 2.74 |
| 2. | Flexural Strength | 40% | 15% | 35 mm | 5% | 68.6 MPa | 68.3 MPa | 0.3 MPa | ±0.95 MPa | 0.44 |
| 3. | Impact Strength | 40% | 15% | 25 mm | 35% | 46.1 kJ/m2 | 39.7 kJ/m2 | 6.4 kJ/m2 | ±9.35 kJ/m2 | 13.88 |
| 4. | Density | 10% | 5% | 5 mm | 15% | 0.5765g/cm3 | 0.5701g/cm3 | 0.0064g/cm3 | 0.0473g/cm3 | 1.11 |
| S/N . | Effects . | Optimum combination . | Predicted Opt. effect . | Confirmed Opt. effect . | Diff. . | Con. Int. . | % Error . | |||
|---|---|---|---|---|---|---|---|---|---|---|
| A . | B . | C . | D . | |||||||
| 1. | Tensile Strength | 20% | 15% | 25 mm | 10% | 82.36 MPa | 80.1 MPa | 2.26 MPa | ±5.134 MPa | 2.74 |
| 2. | Flexural Strength | 40% | 15% | 35 mm | 5% | 68.6 MPa | 68.3 MPa | 0.3 MPa | ±0.95 MPa | 0.44 |
| 3. | Impact Strength | 40% | 15% | 25 mm | 35% | 46.1 kJ/m2 | 39.7 kJ/m2 | 6.4 kJ/m2 | ±9.35 kJ/m2 | 13.88 |
| 4. | Density | 10% | 5% | 5 mm | 15% | 0.5765g/cm3 | 0.5701g/cm3 | 0.0064g/cm3 | 0.0473g/cm3 | 1.11 |
| S/N . | Effects . | Optimum combination . | Predicted Opt. effect . | Confirmed Opt. effect . | Diff. . | Con. Int. . | % Error . | |||
|---|---|---|---|---|---|---|---|---|---|---|
| A . | B . | C . | D . | |||||||
| 1. | Tensile Strength | 20% | 15% | 25 mm | 10% | 82.36 MPa | 80.1 MPa | 2.26 MPa | ±5.134 MPa | 2.74 |
| 2. | Flexural Strength | 40% | 15% | 35 mm | 5% | 68.6 MPa | 68.3 MPa | 0.3 MPa | ±0.95 MPa | 0.44 |
| 3. | Impact Strength | 40% | 15% | 25 mm | 35% | 46.1 kJ/m2 | 39.7 kJ/m2 | 6.4 kJ/m2 | ±9.35 kJ/m2 | 13.88 |
| 4. | Density | 10% | 5% | 5 mm | 15% | 0.5765g/cm3 | 0.5701g/cm3 | 0.0064g/cm3 | 0.0473g/cm3 | 1.11 |